MAO (Micro-arc oxidation) films on TC4 Ti-alloy was prepared, and which then subjected to different post-treatments such as silanization sealing and high temperature oxidation. The MAO/TC4 Ti-alloy before and after post-treatments was characterized by SEM and electrochemical workstation in terms of their surface morphology and performance in galvanic corrosion. The results shows that the surface morphology of the micro-arc oxide film is not significantly changed by high temperature oxidation. TC4 Ti-alloy can easily be suffered from galvanic corrosion when contacting with steel, while the galvanic current density and galvanic corrosion sensitivity of TC4 Ti-alloy couple can be reduced after micro-arc oxidation treatment. The galvanic current density of MAO/TC4 Ti-alloy couple is little affected by silanization sealing treatment, but it is obviously reduced by combined treatments of high temperature oxidation and then silanization sealing. Keywords: TC4 Ti-alloy ; high temperature oxidation ; micro-arc oxidation ; galvanic corrosion |
CopyRight 2018-2019 实验室设备网 版权所有 |